Article Sidebar
Published:
Jul 19, 2024DOI:
10.4314/njt.v43i2.12Keywords:
Article Details
Copyright belongs to the Faculty of Engineering, University of Nigeria, Nsukka, Nigeria
The contents of the articles are the sole opinion of the author(s) and not of NIJOTECH.
NIJOTECH allows open access for distribution of the published articles in any media so long as whole (not part) of articles are distributed.
A copyright and statement of originality documents will need to be filled out clearly and signed prior to publication of an accepted article. The Copyright form can be downloaded from https://www.nijotech.com/downloads/COPYRIGHT%20FORM.pdf while the Statement of Originality is in Statement of Originality.pdf (nijotech.com)
For articles that were developed from funded research, a clear acknowledgement of such support should be mentioned in the article with relevant references. Authors are expected to provide complete information on the sponsorship and intellectual property rights of the article together with all exceptions.
It is forbidden to publish the same research report in more than one journal.
Main Article Content
Effect of cellulosic micro- and nano- sized fillers on strength and microstructure of rubber composites
Abstract
The tensile strength of polymer composites is basically influenced by the geometry (size and shape) of the reinforcing material as well as interfacial interaction and bonding between the polymer matrix and reinforcing phase. This work compares the effect of microfillers to nanofillers of coconut husk, bamboo and cotton linter on the tensile strength and microstructure of vulcanized rubber matrix. The various composites were formulated and prepared using filler loading of 5, 10, 15, 20, 25 and 30 parts per hundred of rubber (pphr) in rubber matrix for both micro- and nano- fillers of the various biomass through friction shearing and compression moulding processes. Results revealed that the tensile strength of the nanocomposites predominantly increased from 1.85 MPa for neat sample to maximum values of 3.83, 3.16 and 3.85 MPa respectively for composites with 25pphr of coconut husk cellulosic nanoparticles (NR-CHNC25), 30pphr of bamboo cellulosic nanoparticles (NR-BNC30) and with 25pphr of cotton linter cellulosic nanoparticles (NR-CLNC25) conversely, the tensile strength of their counter microcomposites changes from 1.85MPa for neat sample to maximum values of 1.68, 1.67 and 2.46 MPa for composites with 10pphr of coconut cellulosic microparticles (NR-CHMC10) 15pphr of bamboo cellulosic microparticles (NR-BMC15) and 30pphr of cotton linter cellulosic microparticles (NR-CLMC30) respectively within the loading range employed in this experiment. Scanning Electron Microscope (SEM) images of microcomposites showed cases of microfiller debonding and pull-out from the rubber matrix. Hence the improved tensile strength of nanocomposites over their counterpart microcomposites was attributed to the larger surface area provided by nanofillers for interfacial bonding and effective stress transfer.