Article Sidebar
Published:
Apr 12, 2024DOI:
10.4314/njt.v43i1.2Keywords:
Article Details
Copyright belongs to the Faculty of Engineering, University of Nigeria, Nsukka, Nigeria
The contents of the articles are the sole opinion of the author(s) and not of NIJOTECH.
NIJOTECH allows open access for distribution of the published articles in any media so long as whole (not part) of articles are distributed.
A copyright and statement of originality documents will need to be filled out clearly and signed prior to publication of an accepted article. The Copyright form can be downloaded from https://www.nijotech.com/downloads/COPYRIGHT%20FORM.pdf while the Statement of Originality is in Statement of Originality.pdf (nijotech.com)
For articles that were developed from funded research, a clear acknowledgement of such support should be mentioned in the article with relevant references. Authors are expected to provide complete information on the sponsorship and intellectual property rights of the article together with all exceptions.
It is forbidden to publish the same research report in more than one journal.
Main Article Content
Compressive, bending and shear properties of reinforced concrete beams containing sawdust ash as partial replacement of cement
Abstract
150x600 mm for the bending test and 150x150x450 mm for the shear test) specimens were used for this investigation. The concrete cube and RC beam specimens had SDA as a partial cement replacement within the range of 0%–10% by weight of cement at 2.5% intervals. 120 RC beam specimens were cast, followed by curing and testing at 28, 60, 90, and 180 days. Using the 4-point loading method, the bending and shear responses of the beams and associated parameters, like the formation and growth of cracks, were determined during the testing. The impact of SDA replacement on the characteristics of fresh and hardened concrete was also assessed using 105 cube specimens cast, cured, and tested at 7, 14, 21, 28, 60, 90, and 180 days. A concrete mix ratio of 1:1.3:2.4 and a constant water/binder ratio of 0.50 at optimum 5% SDA replacement produced (25 N/mm2 ) the required compressive strength. The results show that workability decreases as the SDA percentage increases. Generally, the values of concrete’s densities containing SDA in the mix were in the range of standard weight applications. At 28 days, samples up to 5% recorded a higher compressive, bending, and shear strength development rate than the control mix. The results show that cement partially replaced with up to 5% SDA can produce RC that meets the requirements for concrete for structural application.