Article Sidebar
Published:
Aug 11, 2023DOI:
10.4314/njt.v42i2.10Keywords:
Article Details
Copyright belongs to the Faculty of Engineering, University of Nigeria, Nsukka, Nigeria
The contents of the articles are the sole opinion of the author(s) and not of NIJOTECH.
NIJOTECH allows open access for distribution of the published articles in any media so long as whole (not part) of articles are distributed.
A copyright and statement of originality documents will need to be filled out clearly and signed prior to publication of an accepted article. The Copyright form can be downloaded from https://www.nijotech.com/downloads/COPYRIGHT%20FORM.pdf while the Statement of Originality is in Statement of Originality.pdf (nijotech.com)
For articles that were developed from funded research, a clear acknowledgement of such support should be mentioned in the article with relevant references. Authors are expected to provide complete information on the sponsorship and intellectual property rights of the article together with all exceptions.
It is forbidden to publish the same research report in more than one journal.
Main Article Content
Synthesis and characterization of mehtylammonium bismuth iodide via solvent engineering
Abstract
Hybrid organic–inorganic halide perovskites (OIHPs) are an emerging class of photovoltaic materials that have gained tremendous attention in the field of optoelectronics. This work aims to investigate the characteristics of bismuth-based halide perovskite via solvent engineering for solar cell application. A bismuth-based organo-inorganic perovskite was synthesized and characterized for solar cell application via solvent engineering using Gamma Butyrolactone (GBL) as the based solvent and enhanced with Methylamine (MA) and acetonitrile (ACN). A solution processing facile method was adopted in the synthesis of the perovskite. The solvent engineering aims to tune its band gap and a remarkable band gap of 1.58eV which is within the range of an ideal band gap (1.5-1.6) required for solar cell application. The XRD micrograph exhibited several narrow sharp peaks which indicated crystallinity formation of the synthesized sample with 86% crystallinity. The FESEM/EDS micrograph indicated nature of the formed crystals and the chemical composition of the sample. A multilayer heptagonal crystal was observed. The TGA result showed that the sample is thermally stable at a temperature of 200oC before degradation occurred.