Article Sidebar
Published:
Sep 16, 2020DOI:
10.4314/njt.v39i3.11Keywords:
Article Details
Copyright belongs to the Faculty of Engineering, University of Nigeria, Nsukka, Nigeria
The contents of the articles are the sole opinion of the author(s) and not of NIJOTECH.
NIJOTECH allows open access for distribution of the published articles in any media so long as whole (not part) of articles are distributed.
A copyright and statement of originality documents will need to be filled out clearly and signed prior to publication of an accepted article. The Copyright form can be downloaded from https://www.nijotech.com/downloads/COPYRIGHT%20FORM.pdf while the Statement of Originality is in Statement of Originality.pdf (nijotech.com)
For articles that were developed from funded research, a clear acknowledgement of such support should be mentioned in the article with relevant references. Authors are expected to provide complete information on the sponsorship and intellectual property rights of the article together with all exceptions.
It is forbidden to publish the same research report in more than one journal.
Main Article Content
Performance of metakaolin based geopolymer concrete at elevated temperature
Abstract
Due to the carbon dioxide emission arising from the production of cement, alternative concrete that is environmentally friendly such as metakaolin geopolymer concrete have been developed. However, the performance of metakaolin based geopolymer concrete (MKGC) when exposed to aggressive environment particularly elevated temperature has not been investigated. Therefore, this paper assessed the performance of MKGC exposed to elevated temperatures. MKGC cube specimens of grade 25 were produced using a mix ratio of 1:1.58:3.71.After preparing the specimens, they were placed in an electric oven at a temperature of 60oC for 24 hours. Thereafter, the specimens were stored in the laboratory at ambient temperature for 28 days. The specimens were then exposed to elevated temperatures of 200, 400, 600 and 800oC. After exposure to elevated temperatures, the MKGC specimens were subjected to compressive strength, water absorption and abrasion resistance tests. Results show that at 600 and 800oC, the MKGC lost a compressive strength of 59.69% and 71.71% respectively. Higher water absorption and lower abrasion resistance were also observed.
Keywords: Cement, Compressive Strength, Metakaolin Concrete, Elevated Temperature.