Article Sidebar
Article Details
Copyright belongs to the Faculty of Engineering, University of Nigeria, Nsukka, Nigeria
The contents of the articles are the sole opinion of the author(s) and not of NIJOTECH.
NIJOTECH allows open access for distribution of the published articles in any media so long as whole (not part) of articles are distributed.
A copyright and statement of originality documents will need to be filled out clearly and signed prior to publication of an accepted article. The Copyright form can be downloaded from https://www.nijotech.com/downloads/COPYRIGHT%20FORM.pdf while the Statement of Originality is in Statement of Originality.pdf (nijotech.com)
For articles that were developed from funded research, a clear acknowledgement of such support should be mentioned in the article with relevant references. Authors are expected to provide complete information on the sponsorship and intellectual property rights of the article together with all exceptions.
It is forbidden to publish the same research report in more than one journal.
Main Article Content
Extract of Combretum micranthum as corrosion inhibitor for Al – Si – Mg alloy in simulated sea water environment
Abstract
The leaf extract of Combretum micranthum (CM) was tested as green corrosion inhibitor for Al-Si-Mg alloy in 3.5wt% NaCl solution using gravimetric and linear polarization methods at 300C, 500C and 700C, from 1, 2, 3, 4, 5 hours of exposure time with concentration of the extract 0, 0.2, 0.4, 0.6, 0.8 and 1.0 v/v respectively. The result obtained indicate that the leaf extract of CM is a good corrosion inhibitor in the simulated sea water medium. The inhibition efficiency of the extract increased with an increase in concentration of the CM extract and decreased with increase in temperature. On the other hand, inhibition efficiency (IE%) synergistically decreased on addition of surfactant (Monoethylamine). The adsorption of the inhibitor on Al-Si-Mg surface is exothermic, Spontaneous and is best described by Langmuir, Freundlick and El-Awady adsorption models. The calculated values of activation energy, enthalpy of activation entropy of activation, free energy of process is by physical adsorption. Equally, methanol extract CM is a good adsorption inhibitor for the corrosion of Al-Si-Mg in 3.5wt% NaCl solution. Tafel polarization analysis indicates that the studied plant extract is a mixed type inhibitor.