Article Sidebar
Published:
Dec 25, 2015DOI:
10.4314/njt.v35i1.1Keywords:
Article Details
Copyright belongs to the Faculty of Engineering, University of Nigeria, Nsukka, Nigeria
The contents of the articles are the sole opinion of the author(s) and not of NIJOTECH.
NIJOTECH allows open access for distribution of the published articles in any media so long as whole (not part) of articles are distributed.
A copyright and statement of originality documents will need to be filled out clearly and signed prior to publication of an accepted article. The Copyright form can be downloaded from https://www.nijotech.com/downloads/COPYRIGHT%20FORM.pdf while the Statement of Originality is in Statement of Originality.pdf (nijotech.com)
For articles that were developed from funded research, a clear acknowledgement of such support should be mentioned in the article with relevant references. Authors are expected to provide complete information on the sponsorship and intellectual property rights of the article together with all exceptions.
It is forbidden to publish the same research report in more than one journal.
Main Article Content
ESTIMATING FORMWORK STRIKING TIME FOR CONCRETE MIXES
Abstract
In this study, we estimated the time for strength development in concrete cured up to 56 days. Water-cement ratios adopted range from 0.44-0.57. Nonlinear regression analysis performed on each experimental data set produced Strength-Age (S-A) curves from which Duration-Strength (D-S) models were deduced to estimate approximate time in hours for a particular strength development. A quick reference table for soffit formwork striking time and removal of props was produced. The time to attain the characteristic strengths for C20, C25, C30 and, C35 concrete were 247.04 hours (10.3 days), 285.57 hours (11.90 days), 484.54 hours (20.20 days), 481.58 hours (20.10 days) and, 267.72 hours (11.16 days), 338.74 hours (14.11 days), 560.67 hours (23.36 days), 482.49 hours (20.10 days) for medium and high slump range respectively. Faster construction scheduling operations can be achieved by using lower water-cement ratios and higher grades of concrete.