Tanzania Journal of Engineering and Technology (Tanz. J. Engrg. Technol.) publications are written as a basis for academic discussions. Whereas effort is made by the Editorial Board to screen out inaccurate or misleading statements, data or opinions, Tanz. J. Engrg. Technol. wishes to make it clear that the contents of the articles are the sole responsibility of the authors. Accordingly, the Editorial Board and editors, publisher, College of Engineering and Technology and the University of Dar es Salaam accept no responsibility or liability whatsoever for the opinions, inaccurate or misleading data or statement and views expressed by the authors.
However, the College of Engineering and Technology, the publisher of the Journal, reserve all rights of the articles published in the Journal. Whereas the contents of the articles are available electronically without cost, no part of the publication may be transmitted in any form or reproduced electronically or mechanically, except for short extract in critical scholarly review, research or discourse with an acknowledgement.
Main Article Content
Effects of Calcination Temperature of Naturally Occurring Absorbents on Drinking Water Defluoridation
Abstract
Currently, in Tanzania, fluoride removal from drinking water is treated mostly using the bone char method. The method has poor acceptability in some religious communities and also causes water quality deterioration in taste and odour if the bones are not properly prepared. The use of local natural adsorbents as an alternative is feasible with limitations of high levels of other impurities in treated water. Locally available gypsum, magnesite and bauxite were converted to adsorbents through calcination. The study was conducted to determine the removal efficiency, best calcination temperature and composite ratio of the three adsorbents for the removal of fluoride from natural drinking water with fluoride concentration as high as 16.7 mg/L. The adsorbent materials were calcined at different temperatures ranging between 3500C and 6000C. Batch experiments were performed and samples were collected at different contact time intervals of 2 minutes to 60 minutes, and residual fluoride was determined. Bauxite had the highest fluoride removal efficiency compared to gypsum and magnesite. The best calcination temperatures were 3500C, 4000C, 6000C for gypsum, bauxite and magnesite, respectively. The best calcination temperatures were used to prepare composites at different ratios of 1:2:3, 2:3:1 and 3:2:1, bauxite: gypsum: magnesite respectively. All the ratios gave low sulphate and iron as impurities within the recommended standards. The composites lowered fluoride concentration level to 1.53 mg/L, 2.07 mg/L, 2.60 mg/L for 1:2:3, 2:3:1, 3:2:1 ratios, respectively. In conclusion the study reveals that, it is possible for composites made of adsorbent calcinated at different optimum temperatures to give good results in fluoride removal from drinking water, as well as standard pH, iron and sulphate values in treated water.