In accordance with the Copyright Act of 1976, which became effective January 1, 1978, the following statement signed by each author must accompany the manuscript submitted: "I, the undersigned author, transfer all copyright ownership of the manuscript referenced above to the Nigerian Journal of Technological Development, in the event the work is published. I warrant that the article is original, does not infringe upon any copyright or other proprietary right of any third party, is not under consideration by another journal, and has not been published previously. I have reviewed and approve the submitted version of the manuscript and agree to its publication in the Nigerian Journal of Technological Development." A copyright transfer form may be downloaded from the NJTD Website (http://njtd.com.ng/index.php/njtd). Author(s) will be consulted, whenever possible, regarding republication of material. All authors must have access to the data presented and the authors and sponsor (if applicable) must agree to share original data with the editor if requested.
Main Article Content
Morphological, Mechanical and Thermal Characteristics of PLA /Cocos nucifera L Husk and PLA/Zea mays Chaff Lignin Fibre Mats Composites
Abstract
Polylactide (PLA) is a biodegradable polymer with low elongation which limits its use in some applications. The incorporation of biowaste particles has been employed to improve its properties. This work thus examines the impact of lignin particles reinforced on electrospun PLA fibre mats. Acid hydrolysis (1M of HCl at 60 and 100 oC for 2 and 4 h was used to extract lignin from Cocos nucifera L (CNHL) and Zea Mays Chaff (CCL). Lignin particles were added to molten PLA, stirred, and electrospun at 26 kV, using a static aluminum collector plate placed at 121mm from the spinneret tip. Morphological examination reveals that fibre diameter of neat PLA (9.7 µm) increased from 107 – 285 % with the additions of reinforcements. Maximum tensile strength of 1.03 MPa is recorded for PLA/CNHL 60oC /2 h. This composite maintains the highest elongation of 0.069 % compared to neat PLA (0.046 %). X-Ray diffractometer (XRD) result informs that the crystallinity of neat PLA (67.6 %) improves by 3%, with the use of CNHL 60 oC/ 2 h. Thermo gravimetric analysis (TGA) result shows that both fibre composites possess better thermal stability (380 oC) compared to reinforcing PLA fibre (319 oC).