In accordance with the Copyright Act of 1976, which became effective January 1, 1978, the following statement signed by each author must accompany the manuscript submitted: "I, the undersigned author, transfer all copyright ownership of the manuscript referenced above to the Nigerian Journal of Technological Development, in the event the work is published. I warrant that the article is original, does not infringe upon any copyright or other proprietary right of any third party, is not under consideration by another journal, and has not been published previously. I have reviewed and approve the submitted version of the manuscript and agree to its publication in the Nigerian Journal of Technological Development." A copyright transfer form may be downloaded from the NJTD Website (http://njtd.com.ng/index.php/njtd). Author(s) will be consulted, whenever possible, regarding republication of material. All authors must have access to the data presented and the authors and sponsor (if applicable) must agree to share original data with the editor if requested.
Main Article Content
Optimisation of synthesis parameters for Co-Mo/MgO catalyst yield in MWCNTs production
Abstract
This study examined the impact of synthesis parameter on Cobalt-Molybdenum supported with magnesium oxide (Co-Mo/MgO) catalyst yield in production of multiwall carbon nanotube (MWCNT). Wet impregnation was used to synthesis the Co-Mo/MgO bimetallic catalyst, while a catalytic chemical vapour deposition reactor (CCVD) was used for the synthesis of carbon nanotubes (CNTs). Factorial and central composite design techniques were used to optimise the catalyst and multi-wall carbon nanotubes (MWCNTs). Thermogravimetric analysis/ Differential thermal analysis (TGA/DTA), selected area (electron) diffraction (SAED), X-Ray diffraction analysis (XRD), and Brunauer–Emmett–Teller (BET) were used to characterise the catalyst and MWCNTs that were produced. The Co-Mo/MgO catalyst had an optimal yield of 93.22%, 247.30 m2/g of specific surface area at 120 °C drying temperature, 16 g of mass support, and a 10-hour drying time. The maximum catalyst yield of 40.62% was obtained at calcination temperature of 500 °C and a holding period of 2 hours. The catalyst with the highest degradation temperature of 398.21 °C was observed at 600 °C, when calcined for 4 hours. It was discovered that the surface area of Co-Mo/MgO catalyst from the BET analysis under ideal conditions varied depending on the holding time. The XRD and SAED revealed the growth of CNTs of concentric graphene pattern with the Co-Mo/MgO catalyst.