The copyright of a submitted article is only transferred to the publishers if and when the article is accepted for publication. All rights reserved. No part of this publication may be reproduced, stored in a retrieval system or transmitted in any form or by any means, electronic, electrostatic, mechanical, photocopying, recording or otherwise without the prior written permission of the publishers.
Main Article Content
Improving mechanical properties of aluminium alloy through addition of coconut shell-ash
Abstract
This paper investigates the microstructure and mechanical properties of aluminum alloy (Al-Si-Fe) reinforced with coconut shell-ash particulate. The aluminium (Al-Si-Fe) alloy composite was produced by a double-stir casting process at a speed of 700 rpm for 10 and 5 minutes at first and second stirring respectively. The samples produced from addition of 0-15 wt% coconut shellash particles (CSAp) were prepared and subjected to microstructural and mechanical properties testing. The results of the microstructural analysis of the composite reveal a fairly uniform distribution of the coconut shell-ash particles in the matrix with increase in volume fraction of CSAp. The mechanical property test results revealed that, hardness of the developed composite increased with increasing percentage weight of CSAp. Also the tensile and yield strength at 0.2% offset values of Al-Si-Fe/CSAp composite increased with percentage increase in CSAp up to 9% addition above which a little decrease in both tensile and yield strength was observed.
Keywords: Matrix, coconut shell, mechanical properties, stir- casting, particulate, reinforcements