Submission of a paper for publication implies the transfer of the copyright from the author(s) to the publisher upon acceptance. International Formulae Group is therefore the copyright holder after publication of an article in International Journal of Biological and Chemical Sciences, and published articles should not be used for commercial purpose without the written consent of the Editor-in-Chief. They are licensed under a Creative Commons Attribution-Non Commercial-Share Alike 4.0 International License.
Main Article Content
Study of lifetime of Platinum Modified Metal Oxides Electrodes
Abstract
Pt, IrO2, RuO2, Pt-IrO2 and Pt-RuO2 electrodes have been shown to be effective in their application in various fields. However, it is necessary to study their long-term stability. So, our objective is to prepare them and study their lifetime using intensiostatic measurement. Then they were prepared at 400 °C on titanium plates used as a substrate. Physical measurements (scanning electron microscopy) of these anodes revealed that their surface are rough and porous structures. Lifetime study was carried out in H2SO4 9 N and under a current density of 410 mA /cm2. The long-term stability of Pt improved when coupled to IrO2 in contrast to RuO2. From this study, the performance of the electrode was found to increase in the order: RuO2 < Pt-RuO2 < Pt < Pt-IrO2 < IrO2. For RuO2 and IrO2 pure electrodes, the deactivation would be due to the dissolution of precursors deposited on the titanium. For the Pt pure electrode, deactivation would be due to the detachment of platinum coating. The deactivation of the Pt-IrO2 and Pt-RuO2 electrode would be due, on the one hand to the platinum detachment from IrO2 or RuO2 and on the other hand to the metal oxides (IrO2 or RuO2) dissolution.
Keywords: Electrodes, platinum, metal oxides, lifetime.